Recycling of Ti6Al4V machining swarf into additive manufacturing feedstock powder to realise sustainable recycling goals

Dhiman, Sahil and Joshi, Ravinder Singh and Singh, Sachin and et al, . (2022) Recycling of Ti6Al4V machining swarf into additive manufacturing feedstock powder to realise sustainable recycling goals. Journal of Cleaner Production, 348. ISSN 0959-6526

Full text not available from this repository. (Request a copy)

Abstract

This paper addresses the imperative need to develop sustainable recycle technologies for high value machining swarf generated during the processing of Ti6Al4V alloy. A novel recycling process based on multi-stage ball milling is proposed. The process converts Ti6Al4V swarf into a powder feedstock suitable for additive manufacturing (AM). The powders produced from the cleaned swarf using an in-house designed and fabricated tumbler ball mill were characterised in terms of their morphology, particle size, flowability and spreadability. It was found that the dominant effect of milling with Ø 25 mm balls was particle size reduction (up to ∼ 40%) and the primary effect with smaller balls of Ø 6.25 mm was modification of particle morphology from irregular to rounded shape; thus, necessitating adoption of a multi-stage milling approach to achieve required size and morphology. Ti6Al4V powder having particle size in the range of 40–200 μm and near-spherical morphology was obtained after multi-stage ball milling up to 18 h. The powder characteristics were comparable or superior to the powder produced by generally used gas atomization (GA) process. The suitability of the powders for AM was established through direct metal laser sintering (DMLS). The proper melting of the optimally prepared powder occurs at 1000 mm/s scanning speed and 310 W of laser power. The developed multi-stage ball milling process was assessed vis-à-vis gas atomization using life cycle assessment (LCA). LCA revealed that the proposed ball milling method consumed lower energy (∼59%), had lower eco-cost (∼82%), and lesser global warming potential (GWP) (∼68%). © 2022 Elsevier Ltd

[error in script]
IITH Creators:
IITH CreatorsORCiD
Item Type: Article
Uncontrolled Keywords: Additive manufacturing; Direct metal laser sintering; Life cycle assessment; Machining waste; Recycling; Ti6Al4V
Subjects: Physics > Mechanical and aerospace
Others > Metallurgy Metallurgical Engineering
Divisions: Department of Mechanical & Aerospace Engineering
Depositing User: . LibTrainee 2021
Date Deposited: 28 Jun 2022 04:17
Last Modified: 28 Jun 2022 05:47
URI: http://raiith.iith.ac.in/id/eprint/9414
Publisher URL: http://doi.org/10.1016/j.jclepro.2022.131342
OA policy: https://v2.sherpa.ac.uk/id/publication/13808
Related URLs:

    Actions (login required)

    View Item View Item
    Statistics for RAIITH ePrint 9414 Statistics for this ePrint Item