Wire arc additive manufacturing of functionally graded material with SS 316L and IN625: Microstructural and mechanical perspectives

Sasikumar, R. and Kannan, A. Rajesh and Kumar, S. Mohan and Pramod, R. and Kumar, N. Pravin and Shanmugam, N. Siva and Palguna, Yasam and et al, . (2022) Wire arc additive manufacturing of functionally graded material with SS 316L and IN625: Microstructural and mechanical perspectives. CIRP Journal of Manufacturing Science and Technology, 38. pp. 230-242. ISSN 1755-5817

[img] Text
Manufacturing_Science_and_Technology.pdf - Published Version
Restricted to Registered users only

Download (20MB) | Request a copy

Abstract

In the present study, functionally graded material (FGM) of Austenitic Stainless Steel-SS 316L and Nickel-based superalloy-Inconel 625 (IN625) was manufactured via Gas Metal Arc Welding (GMAW) based Wire Arc Additive Manufacturing (WAAM). WAAM processed FGM was well-formed without any defects and solidification cracking was not observed at the bi-metallic interface (IF) region. Microstructural features show a sharp transition at the IF with a discontinued dendritic structure. Energy-dispersive X-ray spectroscopy (EDS) examination confirmed the fine dissolution of elements at the IF and no major difference in the composition was observed. Electron Backscatter Diffraction (EBSD) maps confirmed that the grains are dominantly columnar while the IF revealed the smooth crystallographic growth along with large elongated dendrites in the< 001 >direction. The microstructure was mainly austenitic in the SS 316L layers with a lower fraction of ferrite while precipitates were noticed in the IN625 layers within the austenitic matrix. Yield strength (YS) and tensile strength (UTS) of SS 316L and IN625 were comparable with wrought ones. All the IF samples at 90° failed in the SS 316L region because of the lower UTS in comparison to IN625 and the mode of fracture was ductile. Microhardness measurements depicted the gradual change of hardness along the building direction. The present work highlights the potential of WAAM to fabricate FGM with required properties and is a viable manufacturing alternative to the traditional manufacturing techniques for producingFGM's. © 2022 CIRP

[error in script]
IITH Creators:
IITH CreatorsORCiD
Item Type: Article
Additional Information: The authors gratefully acknowledge the support of the DST-FIST ( SR/FST/ETI-421/2016 ) SEM-EDS facility at Indian Institute of Technology Hyderabad (IITH). In addition, we wish to thank Dr. Rajesh Korla, Department of Materials Science and Metallurgical Engineering at IITH, for giving access to the lab facility.
Uncontrolled Keywords: EBSD; Functionally graded material; Mechanical properties; Microstructure; Wire arc additive manufacturing
Subjects: Materials Engineering > Materials engineering
Divisions: Department of Material Science Engineering
Depositing User: . LibTrainee 2021
Date Deposited: 18 Oct 2022 10:07
Last Modified: 18 Oct 2022 10:07
URI: http://raiith.iith.ac.in/id/eprint/11007
Publisher URL: http://doi.org/10.1016/j.cirpj.2022.05.005
OA policy: https://v2.sherpa.ac.uk/id/publication/13740
Related URLs:

    Actions (login required)

    View Item View Item
    Statistics for RAIITH ePrint 11007 Statistics for this ePrint Item