Microstructure and Texture of Al-2.5wt.%Mg Processed by Combining Accumulative Roll Bonding and Conventional Rolling

Gatti, J R and Bhattacharjee, P P (2014) Microstructure and Texture of Al-2.5wt.%Mg Processed by Combining Accumulative Roll Bonding and Conventional Rolling. Journal of Materials Engineering and Performance. 10p. ISSN 1059-9495

Full text not available from this repository. (Request a copy)

Abstract

Evolution of microstructure and texture during severe deformation and annealing was studied in Al-2.5%Mg alloy processed by two different routes, namely, monotonic Accumulative Roll Bonding (ARB) and a hybrid route combining ARB and conventional rolling (CR). For this purpose Al-2.5%Mg sheets were subjected to 5 cycles of monotonic ARB (equivalent strain (εeq) = 4.0) processing while in the hybrid route (ARB + CR) 3 cycle ARB-processed sheets were further deformed by conventional rolling to 75% reduction in thickness (εeq = 4.0). Although formation of ultrafine structure was observed in the two processing routes, the monotonic ARB—processed material showed finer microstructure but weak texture as compared to the ARB + CR—processed material. After complete recrystallization, the ARB + CR-processed material showed weak cube texture ({001}〈100〉) but the cube component was almost negligible in the monotonic ARB-processed material-processed material. However, the ND-rotated cube components were stronger in the monotonic ARB-processed material-processed material. The observed differences in the microstructure and texture evolution during deformation and annealing could be explained by the characteristic differences of the two processing routes.

[error in script]
IITH Creators:
IITH CreatorsORCiD
Item Type: Article
Uncontrolled Keywords: accumulative roll bonding; conventional rolling; EBSD; microstructure; severe plastic deformation; texture
Subjects: Materials Engineering > Materials engineering
Divisions: Department of Material Science Engineering
Depositing User: Team Library
Date Deposited: 02 Dec 2014 04:35
Last Modified: 02 Dec 2014 04:35
URI: http://raiith.iith.ac.in/id/eprint/1096
Publisher URL: http://dx.doi.org/10.1007/s11665-014-1237-8
Related URLs:

Actions (login required)

View Item View Item
Statistics for RAIITH ePrint 1096 Statistics for this ePrint Item